| 粘接剂与基牙颜色对三种CAD/CAM全瓷贴面颜色的影响 |
| the effect of shades of luting cements and abutments on the colors of three CAD/CAM all-ceramic laminate materials |
| 投稿时间：2013-02-27 修订日期：2013-04-16 |
| DOI：10.11752/j.kqcl.2013.04.02 |
| 中文关键词: 全瓷贴面 粘接剂 基牙颜色 色差 |
| 英文关键词:All-ceramic laminate Adhesives Abutment's color Color difference |
| 基金项目:上海市科学技术委员会基金资助项目(11ZR1420200); 上海市重点学科建设项口(T0202, 530206) |
|
| 摘要点击次数: 1208 |
| 全文下载次数: 0 |
| 中文摘要: |
| 目的: 评价全瓷修复体材料、基牙颜色及粘接剂oi接对CAD/CAM椅旁系统修复体色泽的影响。方法: 选择s三种CAD/CAM倚旁全瓷修复材料:IPS Empress CAD, IPS E.max CAD和Cerec Blocs。每种材料各制备出以度为(0.8±0.02)mm的试样18片，随机分为3组，以聚四氟乙烯为模板，制作15mm×13mm×2mm的3种颜色的从牙树脂试件，分别采用2种颜色(Transparent与Bleach)的粘接瓷片与基牙树脂，每组三片，静压2min,光照20s,使用台式分光亮度仪测量三种全瓷材料的透光度，比较粘接前后修复体的L*、a*、b*值，并计算粘接前后的色差ΔE。结果: 不管基牙颜色或瓷片种类如何，透明色粘接剂粘接前后的色差皆大于漂白色粘接剂组。Cerec Blocs组粘接前后的色差最大，ΔE.max组的色差最小，而Empress则介于两者之间。结论: 三种全瓷材料中，Empress 的透光最佳，Cerec Blocs陶瓷材料最易受基牙颜色与粘接剂的影响。透明色粘接剂对基牙树脂与磁贴而复合体的颜色影响大于白色粘接剂。 |
| 英文摘要: |
| Objective: the purpose of this study was to evaluate the effect of the shades of cements and abutments on the colors of there kinds of CAD/CAM all-ceramic materials. Methods: Three CAD/CAM chair side all-ceramic restorative materials were selected: IPS Empress CAD, IPS E. max CAD and Cerec Blocs. 18 specimens with a thickmss of (0.8±0.02) mm were prepared from each material. and were randomly divided into three groups. Resin samples of three diilerrnt colors with a size of15mm × 13mm×2mm were produced to simelate abutments ofdifferent colors. The cements oftransparent and bleach colors were used to lute the three kinds of ceramic specimens and the two kinds of ahutment resin samples respectively. After the ceramic specimens were pressed on the resin samples for 2min and light cured for 20s, the translucency of the all-ceramic restorations was measured with a spectrophotometer, and the values of L*, a*and b*before and after bonding were measured and the color difference(ΔE) were calculated. Results: Regardless of the type of abutments or cement colors, ΔE of the transparent adhensive groups was significantly greater than that of the hleach adhesives groups. Cerec Blocs group got the highest color difference before and after bonding, while the color difference before and after bonding for the IPS e. max CAD group was the lowest. Conclusions Among the three types of all-ceramic materials, IPS Empress CAD has the best translucency. The color of Cerec Blocs restorations is more easily been influenced by the shades of abutments and cements. Transparent color cement has more influence on the shade of ceramic-resin complex than the bleach color cement. |